From: Modelling plastic deformation in a single-crystal nickel-based superalloy using discrete dislocation dynamics
Orientation
E (GPa)
v
b (nm)
B (Pa s)
τ F (MPa)
χ APB (mJ/m2)
Initial dislocation density (m−2)
<001>
91.92
0.379
0.25
8.3e-6
200
162.5
2.5e + 13
<111>
244.55
0.179