From: Processing of Al2O3–SiCw–TiC ceramic composite by powder mixed electric discharge grinding
S. No. | Pc (g/L) | Dc (%) | Ton (μs) | Vt (m/min) | Vw (m/min) | MRR (mg/min) | Ra (μm) |
---|---|---|---|---|---|---|---|
1 | 24 | 0.56 | 500 | 0.060 | 2.3550 | 21.26 | 0.4893 |
2 | 16 | 0.40 | 200 | 0.045 | 3.1400 | 12.04 | 0.4067 |
3 | 24 | 0.24 | 300 | 0.060 | 2.3550 | 15.89 | 0.2659 |
4 | 24 | 0.56 | 100 | 0.060 | 2.3550 | 12.17 | 0.2578 |
5 | 16 | 0.40 | 400 | 0.075 | 3.1400 | 15.43 | 0.6441 |
6 | 32 | 0.40 | 200 | 0.075 | 3.1400 | 16.48 | 0.5396 |
7 | 24 | 0.56 | 300 | 0.060 | 2.3550 | 21.39 | 0.4939 |
8 | 24 | 0.56 | 300 | 0.060 | 2.3550 | 21.68 | 0.4886 |
9 | 24 | 0.56 | 300 | 0.060 | 2.3550 | 19.23 | 0.5085 |
10 | 32 | 0.72 | 200 | 0.045 | 3.1400 | 17.45 | 0.3141 |
11 | 24 | 0.88 | 300 | 0.060 | 2.3550 | 28.43 | 0.5277 |
12 | 24 | 0.56 | 300 | 0.060 | 2.3550 | 21.25 | 0.4922 |
13 | 24 | 0.56 | 300 | 0.060 | 2.3550 | 18.76 | 0.4873 |
14 | 16 | 0.72 | 400 | 0.075 | 1.5700 | 13.78 | 1.3706 |
15 | 40 | 0.56 | 300 | 0.060 | 2.3550 | 32.41 | 0.1873 |
16 | 16 | 0.72 | 200 | 0.045 | 1.5700 | 13.92 | 0.9133 |
17 | 24 | 0.56 | 300 | 0.060 | 3.9250 | 21.31 | 0.7466 |
18 | 32 | 0.40 | 400 | 0.045 | 3.1400 | 25.22 | 0.3243 |
19 | 32 | 0.72 | 400 | 0.045 | 1.5700 | 24.25 | 0.2943 |
20 | 24 | 0.56 | 300 | 0.060 | 2.3550 | 18.81 | 0.4984 |
21 | 8 | 0.56 | 300 | 0.060 | 2.3550 | 11.47 | 0.1677 |
22 | 16 | 0.72 | 200 | 0.075 | 3.1400 | 18.35 | 0.4919 |
23 | 32 | 0.72 | 400 | 0.075 | 3.1400 | 48.24 | 0.2522 |
24 | 24 | 0.56 | 300 | 0.090 | 2.3550 | 28.53 | 0.5784 |
25 | 32 | 0.40 | 200 | 0.045 | 1.5700 | 16.62 | 0.3905 |
26 | 24 | 0.56 | 300 | 0.060 | 0.7850 | 14.98 | 0.9711 |
27 | 16 | 0.40 | 400 | 0.045 | 1.5700 | 13.13 | 0.3999 |
28 | 32 | 0.40 | 400 | 0.075 | 1.5700 | 21.88 | 0.5775 |
29 | 24 | 0.56 | 300 | 0.030 | 2.3550 | 17.21 | 0.3889 |
30 | 16 | 0.40 | 200 | 0.075 | 1.5700 | 13.45 | 0.3214 |
31 | 16 | 0.72 | 400 | 0.045 | 3.1400 | 18.82 | 0.7038 |
32 | 32 | 0.72 | 200 | 0.075 | 1.5700 | 32.89 | 0.2807 |