Table 5 Average mechanical properties of tested CFRP laminates
From: The effect of matrix cracking on mechanical properties in FRP laminates
CFRP | Laminates structure | Young’s modulus [GPa] | Tensile strength [MPa] | Max longitudinal strain [%] | Poisson’s ratio |
|---|---|---|---|---|---|
[1] (T700SC/2500) | [03/9024/03] | 30.4 | 523 | 1.96 | 0.031 |
[03/9036/03] | 24.2 | 306 | 1.60 | 0.030 | |
[03/7524/03] | 32.9 | 503 | 1.74 | 0.091 | |
[03/7536/03] | 23.7 | 367 | 1.94 | 0.086 | |
[03/4524/03] | 32.0 | 538 | 1.83 | 0.344 | |
[03/4536/03] | 25.5 | 359 | 1.60 | 0.330 | |
[2] (T700SC/2592) | [0/908/0] | 29.3 | 476 | 1.81 | 0.027 |
[0/9012/0] | 24.5 | 326 | 1.73 | 0.030 | |
[0/608/0] | 29.9 | 516 | 1.87 | 0.218 | |
[0/6012/0] | 24.6 | 360 | 1.75 | 0.227 | |
[0/458/0] | 33.3 | 542 | 1.62 | 0.402 | |
[0/4512/0] | 24.8 | 365 | 1.76 | 0.328 |